Stainless steel pipe polished:welded include Tig welding Stainless Steel Pipes & Mig welding Stainless Steel Pipe,we are professional stainless steel welded tube manufacturers
Specifications of stainless steel pipe polished
1. Product |
Stainless Steel Welded Pipe |
2. Material |
201,202,301,302,304,309,310S,316L,321,347,410,430,409Letc. |
3. Standard |
ASTM, ASME, DIN, EN, ISO,JIS, GOST, etc. |
4. Size range |
OD: from 6mm to 1219mm (NPS from 1/8'' to 40'') |
WT: from 0.7mm to 38mm (Schedule from 5S to XXS) | |
Length: fix length or un-fix length, Max 30meters | |
5. Produce process |
welded,hot bending;resistance welding;Thermal expansion etc. |
6. Surface |
2B,Pickled,180G, 320G, Satin, Hairline,400G, 500G, 600G |
,800G, Mirror finish | |
7. Marking |
SAKY, GRADE, Seamless, Standard, Size, Heat NO. |
8. Package |
Bundles with waterproof cloth outside. |
or plywood box. | |
9. Length |
5.8m,6m,12m or as required |
Typical mechanical properties for 304 stainless steel alloys | |||||
Grade |
Tensile Strength (MPa) |
Compression Strength (MPa) |
Proof Stress 0.2% (MPa) |
Elongation A5 (%) |
Hardness Rockwell B |
304 |
520-720 |
210 |
210 |
45 Min |
92 |
304L |
500-670 |
200 |
45 Min |
||
304H |
520-720 |
210 |
45Min |
Grades of stainless steel pipe polished:
Type |
Grade |
Grade |
Chemical Component % |
||||
Austenitic stainless steel |
C |
Cr |
Ni |
Mn |
|||
201 |
1Cr17Mn6Ni5N |
≤0.15 |
16.00-18.00 |
3.50-5.50 |
5.50-7.50 |
||
201L |
03Cr17Mn6Ni5N |
≤0.030 |
16.00-18.00 |
3.50-5.50 |
5.50-7.50 |
||
202 |
1Cr18Mn8Ni5N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
7.50-10.00 |
||
204 |
03Cr16Mn8Ni2N |
≤0.030 |
15.00-17.00 |
1.50-3.50 |
7.00-9.00 |
||
1Cr18Mn10Ni5Mo3N |
≤0.10 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
|||
2Cr13Mn9Ni4 |
0.15-0.25 |
12.00-14.00 |
3.70-5.00 |
8.00-10.00 |
|||
2Cr15Mn15Ni2N |
0.15-0.25 |
14.00-16.00 |
1.50-3.00 |
14.00-16.00 |
|||
1Cr18Mn10Ni5Mo3N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
|||
301 |
1Cr17Ni7 |
≤0.15 |
16.00-18.00 |
6.00-8.00 |
≤2.00 |
||
302 |
1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
303 |
Y1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
303se |
Y1Cr18Ni9Se |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
304 |
0Cr18Ni9 |
≤0.07 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
304L |
00Cr19Ni10 |
≤0.030 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
||
304N1 |
0Cr19Ni9N |
≤0.08 |
18.00-20.00 |
7.00-10.50 |
≤2.00 |
||
304N2 |
0Cr18Ni10NbN |
≤0.08 |
18.00-20.00 |
7.50-10.50 |
≤2.00 |
||
304LN |
00Cr18Ni10N |
≤0.030 |
17.00-19.00 |
8.50-11.50 |
≤2.00 |
||
305 |
1Cr18Ni12 |
≤0.12 |
17.00-19.00 |
10.50-13.00 |
≤2.00 |
||
309S |
0Cr23Ni13 |
≤0.08 |
22.00-24.00 |
12.00-15.00 |
≤2.00 |
||
310S |
0Cr25Ni20 |
≤0.08 |
24.00-26.00 |
19.00-22.00 |
≤2.00 |
||
316 |
0Cr17Ni12Mo2 |
≤0.08 |
16.00-18.50 |
10.00-14.00 |
≤2.00 |
||
1Cr18Ni12Mo2Ti6) |
≤0.12 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
0Cr18Ni12Mo2Ti |
≤0.08 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
316L |
00Cr17Ni14Mo2 |
≤0.030 |
16.00-18.00 |
12.00-15.00 |
≤2.00 |
||
316N |
0Cr17Ni12Mo2N |
≤0.08 |
16.00-18.00 |
10.00-14.00 |
≤2.00 |
||
316N |
00Cr17Ni13Mo2N |
≤0.030 |
16.00-18.50 |
10.50-14.50 |
≤2.00 |
||
316J1 |
0Cr18Ni12Mo2Cu2 |
≤0.08 |
17.00-19.00 |
10.00-14.50 |
≤2.00 |
||
316J1L |
00Cr18Ni14Mo2Cu2 |
≤0.030 |
17.00-19.00 |
12.00-16.00 |
≤2.00 |
||
317 |
0Cr19Ni13Mo3 |
≤0.12 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
||
317L |
00Cr19Ni13Mo3 |
≤0.08 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
||
1Cr18Ni12Mo3Ti6 |
≤0.12 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
0Cr18Ni12Mo3Ti |
≤0.08 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
317J1 |
0Cr18Ni16Mo5 |
≤0.040 |
16.00-19.00 |
15.00-17.00 |
≤2.00 |
||
321 |
1Cr18Ni9Ti6 |
≤0.12 |
17.00-19.00 |
8.00-11.00 |
≤2.00 |
||
0Cr18Ni10Ti |
≤0.08 |
17.00-19.00 |
9.00-12.00 |
≤2.00 |
|||
347 |
0Cr18Ni11Nb |
≤0.08 |
17.00-19.00 |
9.00-13.00 |
≤2.00 |
||
XM7 |
0Cr18Ni9Cu3 |
≤0.08 |
17.00-19.00 |
8.50-10.50 |
≤2.00 |
||
XM15J1 |
0Cr18Ni13Si4 |
≤0.08 |
15.00-20.00 |
11.50-15.00 |
≤2.00 |
Austenite |
329J1 |
0Cr26Ni5Mo2 |
≤0.08 |
23.00-28.00 |
3.00-6.00 |
≤1.50 |
≤0.035 |
≤0.030 |
1.00-3.00 |
≤1.00 |
- |
- |
2) |
1Cr18Ni11Si4AlTi |
0.10-0.18 |
17.50-19.50 |
10.--120.. |
≤0.80 |
≤0.035 |
≤0.030 |
- |
3.40-4.00 |
- |
- |
Al 0.10-0.30; Ti 0.40-0.70 |
||
00Cr18Ni5MoSi2 |
≤0.030 |
18.00-19.50 |
4.50-5.50 |
1.00-2.00 |
≤0.035 |
≤0.030 |
2.50-3.00 |
1.30-2.00 |
- |
- |
- |
||
Ferrite Stainless Steel |
405 |
0Cr13Al |
≤0.08 |
11.50-14.50 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
Al 0.10-0.30 |
410L |
00Cr12 |
≤0.030 |
11.00-13.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
430 |
1Cr17 |
≤0.12 |
16.00-18.00 |
3) |
≤1.25 |
≤0.035 |
≤0.030 |
- |
≤0.75 |
- |
- |
- |
|
430F |
Y1Cr17 |
≤0.12 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≥0.15 |
1) |
≤1.00 |
- |
- |
- |
|
434 |
1Cr17Mo |
≤0.12 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
0.75-1.25 |
≤1.00 |
- |
- |
- |
|
447J1 |
00Cr30Mo2 |
≤0.010 |
28.50-32.00 |
- |
≤0.40 |
≤0.035 |
≤0.030 |
1.50-2.50 |
≤0.40 |
- |
≤0.015 |
- |
|
XM27 |
00Cr27Mo |
≤0.010 |
25.00-27.50 |
- |
≤0.40 |
≤0.035 |
≤0.030 |
0.75-1.50 |
≤0.40 |
- |
≤0.015 |
- |
Martensite stainless steel |
403 |
1Cr12 |
≤0.15 |
11.50-13.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤0.50 |
- |
- |
- |
410 |
1Cr13 |
≤0.15 |
11.50-13.50 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
405 |
0Cr13 |
≤0.08 |
11.50-13.50 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
416 |
Y1Cr13 |
≤0.15 |
12.00-14.00 |
3) |
≤1.25 |
≤0.035 |
≥0.15 |
1) |
≤1.00 |
- |
- |
- |
|
410J1 |
1Cr13Mo |
≤0.08-0.18 |
11.50-14.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
0.30-0.60 |
≤0.60 |
- |
- |
- |
|
420J1 |
2Cr13 |
0.16-0.25 |
12.00-14.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
420J2 |
3Cr13 |
0.26-0.35 |
12.00-14.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
420F |
Y3Cr13 |
0.26-0.40 |
12.00-14.00 |
3) |
≤1.25 |
≤0.035 |
≥0.15 |
1) |
≤1.00 |
- |
- |
- |
|
3Cr13Mo |
0.28-0.35 |
12.00-14.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
0.50-1.00 |
≤0.80 |
- |
- |
- |
||
4Cr13 |
0.36-0.45 |
12.00-14.00 |
3) |
≤0.80 |
≤0.035 |
≤0.030 |
- |
≤0.60 |
- |
- |
- |
||
431 |
1Cr17Ni2 |
0.11-0.17 |
16.00-18.00 |
1.50-2.50 |
≤0.80 |
≤0.035 |
≤0.030 |
- |
≤0.80 |
- |
- |
- |
|
440A |
7Cr17 |
0.60-0.75 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
4) |
≤1.00 |
- |
- |
- |
|
440B |
8Cr17 |
0.75-0.95 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
4) |
≤1.00 |
- |
- |
- |
|
9Cr18 |
0.90-1.00 |
17.00-19.00 |
3) |
≤0.80 |
≤0.035 |
≤0.030 |
4) |
≤0.80 |
- |
- |
- |
||
440C |
11Cr17 |
0.95-1.20 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
4) |
≤1.00 |
- |
- |
- |
|
440F |
Y11Cr17 |
0.95-1.20 |
16.00-18.00 |
3) |
≤1.25 |
≤0.035 |
≥0.15 |
4) |
≤1.00 |
- |
- |
- |
|
9Cr18Mo |
0.95-1.10 |
16.00-18.00 |
3) |
≤0.80 |
≤0.035 |
≤0.030 |
0.40-0.70 |
≤0.80 |
- |
- |
- |
||
9Cr18MoV |
0.85-0.95 |
17.00-19.00 |
3) |
≤0.80 |
≤0.035 |
≤0.030 |
1.00-1.30 |
≤0.80 |
- |
- |
V0.07-0.12 |
||
PH Stainless Steel |
630 |
0Cr17Ni4Cu4Nb |
≤0.07 |
15.50-17.50 |
6.50-7.50 |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
3.00-5.00 |
- |
Nb 0.15-0.45 |
631 |
0Cr17Ni7Al |
≤0.09 |
16.00-18.00 |
6.50-7.50 |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
≤0.50 |
- |
Al 0.75-1.50 |
|
632 |
0Cr15Ni7Mo2Al |
≤0.09 |
14.00-16.00 |
6.50-7.50 |
≤1.00 |
≤0.035 |
≤0.030 |
2.00-3.00 |
≤1.00 |
- |
- |
Al 0.75-1.50 |
SASA METAL, established in 1995, is an experienced and professional manufacturers and suppliers of stainless steel pipe polished. With the aid of qualified workers and advanced equipment, we can assure you the high quality and good performance of our products. Please be free to buy products for sale with us.